塑膠產(chǎn)品生產(chǎn)時(shí)都會(huì)遇到產(chǎn)品注塑出來(lái)缺膠以及開(kāi)裂的問(wèn)題，今天
山東模具制造廠家就為大家分析一下相關(guān)的應(yīng)對(duì)方法，供大家參考使用。
During the production of plastic products, we will encounter the problems of lack of glue and cracking after injection molding. Today, Shandong mold manufacturers will analyze the relevant countermeasures for your reference.
模具注塑過(guò)程中產(chǎn)品缺膠
The product is short of glue during mold injection
原因一：料溫，模溫太低
Reason 1: the material temperature and mold temperature are too low
改善對(duì)策：是提高，料管溫度和模具溫度。
Improvement measures: increase the temperature of the material pipe and the mold.
原因二：噴嘴，進(jìn)膠點(diǎn)尺寸太小。
Reason 2: the size of nozzle and glue inlet point is too small.
改善對(duì)策：適當(dāng)加大噴嘴及進(jìn)膠點(diǎn)。
Improvement measures: appropriately increase the nozzle and glue inlet point.
原因三：模具排氣不良。
Reason 3: poor mold exhaust.
改善對(duì)策：可增開(kāi)排氣孔。
Improvement measures: open more exhaust holes.
原因四：噴嘴冷頭或者堵塞
Reason 4: nozzle cold head or blockage
改善對(duì)策：可通過(guò)射嘴雜物，提高射嘴溫度來(lái)
Improvement countermeasures: it can be solved by removing sundries from the nozzle and increasing the temperature of the nozzle
原因五：射出速度和壓力不夠
Reason 5: insufficient injection speed and pressure
改善對(duì)策：方法就是提高射速，射壓。
Improvement countermeasures: the solution is to increase the shooting speed and pressure.
模具注塑過(guò)程中產(chǎn)品開(kāi)裂
Product cracking during mold injection
（1）加工壓力過(guò)大、速度過(guò)快、充料愈多、注射、保壓時(shí)間過(guò)長(zhǎng)，都會(huì)造成內(nèi)應(yīng)力過(guò)大而開(kāi)裂。
(1) Too much processing pressure, too fast speed, more filling, and too long injection and pressure holding time will cause excessive internal stress and cracking.
（2）調(diào)節(jié)開(kāi)模速度與壓力防止快速?gòu)?qiáng)拉制件造成脫模開(kāi)裂。
(2) Adjust the mold opening speed and pressure to prevent demoulding cracking caused by rapid strong drawing.
（3）適當(dāng)調(diào)高模具溫度，使制件易于脫模，適當(dāng)調(diào)低料溫防止分解。
(3) Appropriately increase the mold temperature to make the parts easy to demould, and appropriately reduce the material temperature to prevent decomposition.
（4）預(yù)防由于熔接痕，塑料降解造成機(jī)械強(qiáng)度變低而出現(xiàn)開(kāi)裂。
(4) Prevent cracking due to low mechanical strength caused by fusion marks and plastic degradation.
（5）適當(dāng)使用脫模劑，注意經(jīng)常模面附著的氣霧等物質(zhì)。
(5) Use release agent properly, and pay attention to often eliminate the aerosol and other substances attached to the mold surface.
（6）制件殘余應(yīng)力，可通過(guò)在成型后立即進(jìn)行退火熱處理來(lái)內(nèi)應(yīng)力而減少裂紋的生成。
(6) The residual stress of parts can be eliminated by annealing heat treatment immediately after forming to reduce the generation of cracks.
以上總結(jié)是比較有代表性的方面，實(shí)際操作當(dāng)中，可能還會(huì)有其它情況導(dǎo)致的注塑成型問(wèn)題，具體根據(jù)實(shí)際情況。更多相關(guān)內(nèi)容就來(lái)我們網(wǎng)站
http://m.le193.cn咨詢(xún)吧。
The above summary is a representative aspect. In actual operation, there may be injection molding problems caused by other situations, which can be solved according to the actual situation. Come to our website for more relevant content http://m.le193.cn Consult.